Sólido con protección contra gas

Introducción: JQ.MG80-G es una clase de alambre soldado gas-blindado de alta resistencia. El gas mezclado Ar + 20% CO2 puede utilizarse como gas de protección. Tiene arco suave, quema estable y menos salpicaduras. El cordón tiene mayor resistencia al impacto.

Composición química del alambre de soldadura (%)

Shanghai Metal Corporation has been doing business for welding wire for decades. Its products features good quality and durability. 

Welding is a fabrication or sculptural process that joins materials, usually metals or thermoplastics, by causing fusion, which is distinct from lower temperature metal-joining techniques such as brazing and soldering, which do not melt the base metal. 

In addition to melting the base metal, a filler material is typically added to the joint to form a pool of molten material (the weld pool) that cools to form a joint that is usually stronger than the base material. 

Pressure may also be used in conjunction with heat, or by itself, to produce a weld.

Gas-shielded Solid
Introduction: JQ.MG80-G is a kind of high strength gas-shielded welding wire. The mixed gas Ar+20% CO2 can be used as shielding gas. It has soft arc, stable burning and fewer spatters. The bead has higher impact toughness.

Uses: Suitable for welding high strength structures with tensile strength of 790MPa. It can be used for welding some key structures, such as pressure vessels, construction machinery, hoisting machinery, ships, mining machinery, etc.
Chemical Composition of Welding Wire(%)

Ejemplos de composición química del metal depositado (%)

Tamaño del cable

Alambre de soldadura con flujo de gas

JQ YR302

GB: E551T1-B2

AWS: E81T1-B2

Corriente: Conveniente para la soldadura 1Cr0.5Mo (tal como 15CrMo) acero debajo de 520

Aplicaciones principales:

JQ.YR302

Según GB / T 17493 - 1998 E551T1 - B2

Correspondiente a AWS A5.29 E81T1-B2

JIS Z3318 YF1CM-C

Usos: Conveniente para la soldadura 1% Cr-0.5% Mo (tal como 15CrMo) acero debajo de 520 ℃.

Chemical Composition of Deposited Metal (%)(CO2Shielding Gas)

Instrucciones:

1. las manchas de aceite y el óxido en las soldaduras deben despejarse.

2. cuando solda, el caudal de gas es generalmente de 20 ~ 25 l/min.

3. al soldar con alambres de soldadura de núcleo fundente, el alargamiento de la extensión debe ser de 15 ~ 25 mm.

4. la humedad de los almacenes del alambre de la soldadura se debe preservar debajo de 60%.

5. No es adecuado para los cables de soldadura no envasados al vacío que se almacenan durante más de medio año, y no es adecuado para los cables de soldadura envasados al vacío para ser almacenados durante más de un año.

Gas-shielded Flux-cored Welding Wire

JQ. YR302

GB：E551T1-B2

AWS：E81T1-B2

Current：Suitable for welding 1Cr0.5Mo (such as 15CrMo) steel below 520

Main Applications： 

JQ.YR302

According with GB/T 17493-1998 E551T1-B2

Corresponding with AWS A5.29 E81T1-B2

JIS Z3318 YF1CM-C

Uses: Suitable for welding 1％Cr－0.5％Mo (such as 15CrMo) steel below 520℃.

Instructions:

1.The oil stains and rust on the weldments should be cleared away.

2.When welding, the gas flow rate is generally 20～25L/min.

3.When welding with flux-cored welding wires, the extension elongation should be 15～25mm.

4.The humidity of the welding wire storerooms should be preserved below 60%.

5.It is not suitable for non-vacuum-packed welding wires to be stored for more than half a year, and it is not suitable for vacuum-packed welding wires to be stored for more than a year.

Embalaje de alambre de soldadura:

Los productos de Shanghai Metal Corporation se embalan y se etiquetan según las regulaciones y las peticiones del cliente.

Se toma mucho cuidado para evitar cualquier daño que pueda ser causado durante el almacenamiento o el transporte

Además, las etiquetas claras se marcan en el exterior de los paquetes para la identificación del producto I. D. y la información de calidad.

Packaging of Welding Wire:

Shanghai Metal Corporation Products are packed and labeled according to the regulations and customer's requests.

Great care is taken to avoid any damage which might be caused during storage or transportation.

In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.

Se pueden utilizar muchas fuentes de energía diferentes para la soldadura, incluyendo una llama de gas,

un arco eléctrico, un láser, un haz de electrones, fricción y ultrasonido.

Aunque a menudo es un proceso industrial, la soldadura puede realizarse en muchos entornos diferentes,

incluso al aire libre, bajo el agua y en el espacio ultraterrestre.

La soldadura es una tarea peligrosa y se requieren precauciones para evitar quemaduras,

descarga eléctrica, daño visual, inhalación de gases y humos venenosos y exposición a radiación ultravioleta intensa.

Many different energy sources can be used for welding, including a gas flame,

an electric arc, a laser, an electron beam, friction, and ultrasound.

While often an industrial process, welding may be performed in many different environments,

including in open air, under water, and in outer space.

Welding is a hazardous undertaking and precautions are required to avoid burns,

electric shock, vision damage, inhalation of poisonous gases and fumes, and exposure to intense ultraviolet radiation.