Espesor: 0.125mm-3.0mm
Ancho: como su petición
Identificación de la bobina: 100 mm / 508 mm
Thickness: 0.125mm-3.0mm
Width: As your request
Coil ID: 100mm/508mm
Especificación de la tira de acero galvanizada en caliente:
1) Capacidad: alrededor de 15,000 toneladas por mes para el producto de cinta de acero / cinta
2) Grosor: de 0,125 mm a 3,0 mm, todo disponible.
3) Ancho: como su petición
4) Grado: SGHC, Q195, SGCC, DX51D
5) Peso de la bobina: de 50 kg a 7000 kg, todos disponibles.
6) Identificación de la bobina: 100 mm / 508 mm
7) resistencia a la tracción: 28.1-49.2kgf / mm2
8) Peso del recubrimiento de zinc: 30g / m2-600g / m2
9) Lentejuela: lentejuela grande, lentejuela normal, lentejuela pequeña, sin lentejuela
10) Tratamiento superficial: tratamiento de pasivado químico, aceites, pasivación + aceites
11) orden mínima de prueba 5ton cada espesor, 1 x 20 'por entrega
12) Tratamiento superficial de la tira de acero galvanizada en caliente:
Specification of Hot Dip Galvanized Steel Strip:
1) Capacity: about 15,000 ton per month for steel strip/tape product
2) Thickness: from 0.125mm to 3.0mm, all available.
3) Width: As your request
4) Grade: SGHC, Q195, SGCC, DX51D
5) Coil weight: from 50kg to 7000kg, all available.
6) Coil ID: 100mm/508mm
7) Tensile strength: 28.1-49.2kgf/mm2
8) Zinc coating weight: 30g/m2-600g/m2
9) Spangle : big spangle, normal spangle, small spangle, non-spangle
10) Surface treatment: chemical passivating treatment, oils, passivating + oils
11) Min trial order 5ton each thickness, 1 x 20' per delivery
12) Surface Treatment of Hot Dip Galvanized Steel Strip:
13) Lentejuela de la tira de acero galvanizada de la inmersión caliente:
13)Spangle of Hot Dip Galvanized Steel Strip:
14) Característica: La tira / bobina de acero galvanizado en caliente se fabrica para tener una larga durabilidad, una fuerte resistencia a la corrosión y una superficie brillante.
También presenta excelentes propiedades de conformado, capacidad de pintura, soldabilidad y es adecuado para la fabricación mediante formación, prensado y doblado.
14) Feature: Hot Dip Galvanized Steel Strip/Coil is manufactured to have a long durability, strong corrosion resistance and shiny surface.
It is also features excellent forming properties, paintability, weldability, and is suitable for fabrication by forming, pressing and bending.
Introducción:
La banda de acero galvanizado en caliente es tan flexible como nuestros clientes. Nuestro material se produce en cinco líneas de galvanizado por inmersión en caliente en Linz con diversos revestimientos de zinc, calidades de superficie y tratamientos posteriores como aceite, pasivación o antihuellas. Entregado en rollos como una tira de hendidura o formas cortadas.
Presupuesto:
1. Estándar: AISI, ASTM, BS, DIN, GB, JIS;
2. Grade: SGCC, SGCH, G550, DX51D, DX52;
3. Tamaño: Espesor: 0,13-2,5 mm, Ancho: 40 mm-1250 mm.
4. Recubrimiento de zinc: 30-275g / m2;
5. Paquete: paquete de exportación estándar
Solicitud:
La tira de acero galvanizado se utiliza para blindar los cables de potencia. También se usa en C & Z Purlins Industries, Industrias de perfiles de acero, Industrias de placas de conectores Truss, Industrias de placas de uñas, Industrias de abrazaderas de mangueras, Industrias de paneles de acero, Tubos y tuberías y muchas otras Industrias generales.
Proceso
El proceso de galvanizado en caliente da como resultado un enlace metalúrgico entre el zinc y el acero con una serie de distintas aleaciones de hierro y zinc. El acero revestido resultante se puede usar de la misma manera que sin revestir.
Una línea típica de galvanizado por inmersión en caliente funciona de la siguiente manera:
El acero se limpia con una solución cáustica. Esto elimina aceite / grasa, suciedad y pintura.
La solución de limpieza cáustica se enjuaga.
El acero se decapa en una solución ácida para eliminar la escala del molino.
La solución de decapado se enjuaga.
Un flujo, a menudo zinc cloruro de amonio se aplica al acero para inhibir la oxidación de la superficie limpiada al exponerse al aire. El flujo se deja secar en el acero y ayuda en el proceso de la humectación del zinc líquido y la adherencia al acero
El acero se sumerge en el baño de zinc fundido y se mantiene allí hasta que la temperatura del acero se equilibra con la del baño.
El acero se enfría en un tanque de enfriamiento rápido para reducir su temperatura e inhibir las reacciones indeseables del revestimiento recién formado con la atmósfera.
A menudo se agrega plomo al baño de zinc fundido para mejorar la fluidez del baño (limitando así el exceso de zinc en el producto sumergido mediante propiedades mejoradas de drenaje), ayuda a evitar escoria flotante, facilita el reciclaje de escoria y protege la caldera Pilling de una distribución de calor desigual los quemadores El plomo se agrega al zinc primario de grado Z1 o ya está contenido en zinc secundario usado. Un tercer método en declive es usar zinc de bajo grado Z5.
La cinta de acero puede galvanizarse por inmersión en caliente en una línea continua. La banda de acero galvanizado en caliente (también conocida como hierro galvanizado) se usa ampliamente para aplicaciones que requieren la resistencia del acero combinado con la resistencia a la corrosión del zinc. techos y muros, barreras de seguridad, pasamanos, electrodomésticos y partes del cuerpo del automóvil. Un uso común es en cubos de metal. El acero galvanizado también se usa en la mayoría de los sistemas de conductos de calefacción y refrigeración en edificios
Los artículos individuales de metal, como las vigas de acero o las puertas de hierro forjado, pueden galvanizarse por inmersión en caliente mediante un proceso llamado galvanizado discontinuo. Otras técnicas modernas han reemplazado en gran medida a la inmersión en caliente para este tipo de funciones. Esto incluye la electrogalvanización, que deposita la capa de zinc de un electrolito acuoso mediante galvanoplastia, formando un enlace más delgado y mucho más fuerte.
Introduction:
Hot-dip galvanized steel strip is as flexible as our customers. Our material is produced in five hot-dip galvanizing lines in Linz with various zinc coatings, surface qualities and post-treatments such as oil, passivation or anti-fingerprinting. Delivered in coils as slit strip or cut shapes.
Specifications:
1.Standard: AISI, ASTM, BS, DIN, GB, JIS;
2.Grade:SGCC,SGCH,G550,DX51D,DX52;
3. Size:Thickness:0.13-2.5mm, Width:40mm-1250mm.
4.Zinc coating: 30-275g/m2;
5. Package:Standard Export Package
Application:
Galvanized steel strip is used for Armouring of Power Cables. It si also used in C&Z Purlins Industries, Steel Profiles Industries, Truss Connector Plates Industries , Nail Plates Industries, Hose Clamps Industries , Steel Panels Industries , Pipes and Tubes and many other General Industries.
Process
The process of hot-dip galvanizing results in a metallurgical bond between zinc and steel with a series of distinct iron-zinc alloys. The resulting coated steel can be used in much the same way as uncoated.
A typical hot-dip galvanizing line operates as follows:
Steel is cleaned using a caustic solution. This removes oil/grease, dirt, and paint.
The caustic cleaning solution is rinsed off.
The steel is pickled in an acidic solution to remove mill scale.
The pickling solution is rinsed off.
A flux, often zinc ammonium chloride is applied to the steel to inhibit oxidation of the cleaned surface upon exposure to air. The flux is allowed to dry on the steel and aids in the process of the liquid zinc wetting and adhering to the steel.
The steel is dipped into the molten zinc bath and held there until the temperature of the steel equilibrates with that of the bath.
The steel is cooled in a quench tank to reduce its temperature and inhibit undesirable reactions of the newly formed coating with the atmosphere.
Lead is often added to the molten zinc bath to improve the fluidity of the bath (thus limiting excess zinc on the dipped product by improved drainage properties), helps prevent floating dross, makes dross recycling easier and protects the Pilling kettle from uneven heat distribution from the burners. Lead is either added to primary Z1 grade zinc or already contained in used secondary zinc. A third, declining method is to use low Z5 grade zinc.
Steel strip can be hot-dip galvanized in a continuous line. Hot-dip galvanized steel strip (also sometimes loosely referred to as galvanized iron) is extensively used for applications requiring the strength of steel combined with the resistance to corrosion of zinc. roofing and walling, safety barriers, handrails, consumer appliances and automotive body parts. One common use is in metal pails. Galvanised steel is also used in most heating and cooling duct systems in buildings
Individual metal articles, such as steel girders or wrought iron gates, can be hot-dip galvanized by a process called batch galvanizing. Other modern techniques have largely replaced hot-dip for these sorts of roles. This includes electrogalvanizing, which deposits the layer of zinc from an aqueous electrolyte by electroplating, forming a thinner and much stronger bond.
Embalaje para la tira de acero galvanizada en caliente:
Los productos de metal de Shanghai se embalan y etiquetan de acuerdo con las regulaciones y las solicitudes del cliente. Se tiene mucho cuidado para evitar cualquier daño que pueda ser causado durante el almacenamiento o el transporte. Además, las etiquetas transparentes se etiquetan en el exterior de los paquetes para facilitar la identificación del producto I. D. y la información de calidad.
Packaging for Hot Dip Galvanized Steel Strip:
Shanghai Metal Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.
Aplicación de la tira de acero galvanizada en caliente:
1. Construcción y construcción: techado; conducto de ventilación; pretil; panel de partición, etc.
2. Procesamiento adicional: placa base de recubrimiento
3. Dispositivo eléctrico: refrigerador; lavadora; grabadora; microondas, etc.
Preguntas más frecuentes
¿Qué es acero galvanizado?
Hay dos formas típicas de galvanizado para obtener un revestimiento de zinc: galvanizado por inmersión en caliente y electrogalvanización. El galvanizado por inmersión en caliente es el proceso por el cual el acero se sumerge en un baño de zinc fundido para obtener una superficie de recubrimiento de zinc. Esto no solo ayuda a proteger el acero del óxido y la corrosión, sino que también le da al acero un aspecto atractivo y brillante. La electrogalvanización es el proceso que utiliza la electrólisis para recubrir el acero con zinc, que no es rentable ni respetuoso con el medio ambiente. Es difícil encontrar acero electrogalvanizado en nuestras vidas hoy en día.
¿Cuáles son las ventajas del acero galvanizado?
Debido a las capas de aleación de zinc / hierro permanentemente y sucesivas, el acero galvanizado ofrece muchos beneficios que los aceros tradicionales.
>> Resistencia a la corrosión: la superficie de recubrimiento de zinc protege el acero base no solo al proporcionar barrera a los elementos de corrosión, sino también por la naturaleza sacrificial del recubrimiento. El acero galvanizado a menudo permanece en buen funcionamiento con poco mantenimiento durante 40 años o más.
>> Excelente apariencia superficial
>> Formabilidad: se puede doblar simplemente para piezas con requisitos de dibujo profundo.
>> Pintabilidad: se puede pintar con diferentes colores.
>> Soldabilidad: se aceptan diversas prácticas de soldadura.
¿Cuáles son las desventajas del acero galvanizado?
A pesar de los muchos beneficios, el acero galvanizado no siempre es una opción ideal. El acero galvanizado no se puede utilizar bajo tierra sin una cubierta adecuada, lo que puede ser inconveniente para muchos trabajos.
¿Dónde usamos acero galvanizado?
Se utiliza principalmente en la industria de la construcción, como techos, revestimientos de paredes y vigas de soporte. También se usa en la industria automotriz, debido a su capacidad de pintura mejorada, soldabilidad y resistencia a la corrosión. Además, es un material esencial para la aplicación de electrodomésticos, como refrigeradores, acondicionadores de aire, lavadoras, microondas, máquinas expendedoras y sistemas audiovisuales.
Application of Hot Dip Galvanized Steel Strip:
1.Construction and building: roofing; ventilating duct; handrail; partition panel,etc.
2.Further processing: coating base plate
3.Electric appliance: Refrigerator; washing machine; recorder; microwave, etc.
FAQ
What is Galvanized Steel?
There are two typical galvanizing ways to obtain a zinc coating: hot dip galvanizing and electrogalvanizing. Hot dip galvanizing is the process that steel is immersed into molten zinc bath to get a zinc coating surface. This not only helps protect steel from rust and corrosion, but also gives the steel a shiny attractive appearance. Electrogalvanizing is the process that uses electrolysis to coat the steel with zinc, which is neither cost-effective nor environmentally friendly. It is hardly to find electrogalvanized steel in our lives nowadays.
What are advantages of galvanized steel?
Because of permanently and successive zinc/iron alloy layers, galvanized steel offers many benefits than traditional steels.
>>Corrosion Resistance: the zinc coating surface protects the base steel not only by providing barrier to corrosion elements, but also by the sacrificial nature of the coating. Galvanized steel often remains in working order with little maintenance for 40 years or more.
>>Excellent Surface Appearance
>>Formability: it can be simply bend to parts with deep drawing requirements.
>>Paintability: it can be painted with different colors.
>>Weldability: it is accepted various welding practices.
What are disadvantages of galvanized steel?
In spite of many benefits, galvanized steel is not always an ideal choice. Galvanized steel cannot be used underground without properly covered, which can be inconvenient for many jobs.
Where do we use galvanized steel?
It is primarily used in the construction industry, such as roofing, wall cladding, and support beams. It is also used in the automotive industry, due to its enhanced paintability, weldability and corrosion resistance. Moreover, it is an essential material for white goods application, such as refrigerators, air-conditioners, washers, microwaves, vending machines and audio visual systems.